POM H2320巴斯夫POM H2320巴斯夫POM H2320巴斯夫POM H2320巴斯夫POM H2320巴斯夫POM H2320巴斯夫。Product Description
Ultraform H 2320 006 UNC Q600 is a POM with high molecular weight grade for injection molding.
Applications
Typical applications include thick-walled articles.
PHYSICAL ISO Test Method Property Value
Density, g/cm³ 1183 1.40
Mold Shrinkage, parallel, % 294-4 2.1
Mold Shrinkage, normal, % 294-4 2.1
Moisture, % 62
(50% RH) 0.2
(Saturation) 0.8
RHEOLOGICAL ISO Test Method Property Value
Melt Volume Rate (190 C/2.16 Kg), cc/10min. 1133 2.9
MECHANICAL ISO Test Method Property Value
Tensile Modulus, MPa 527
23C 2,600
Tensile stress at yield, MPa 527
23C 64
80C 33
Tensile strain at yield, % 527
23C 11
Nominal strain at break, % 527
23C 30
Flexural Modulus, MPa 178
23C 2,600
Tensile Creep Modulus (1000h), MPa 899 1,300
Tensile Creep Modulus (1h), MPa 899 1,800
IMPACT ISO Test Method Property Value
Izod Notched Impact, kJ/m2 180
-40C 5
23C 6
Charpy Notched, kJ/m2 179
-30C 5.5
23C 6
Charpy Unnotched, kJ/m2 179
-30C 200
23C 260
THERMAL ISO Test Method Property Value
Melting Point, C 3146 166
HDT A, C 75 95